Scientific Reports volume 13, Article number: 11666 (2023) Cite this article

264 Accesses

Metrics details

In this study, we evaluated the impact of xanthan gum biopolymer (XG) on kaolinite fabrics using X-ray diffraction (XRD) and the ensuing changes in the compaction behavior and shear resistance of kaolinite soils. The XRD peak analysis revealed that XG changed kaolinite fabrics into face-to-face associations. Moreover, environmental scanning electron microscopy showed the formation of XG-bridges between kaolinite particles, resulting in the change in fabrics and subsequently improving the resistance of kaolinite to external forces. Consequently, as XG content increased, the maximum dry density decreased, and the undrained shear strength increased. The viscous XG hydrogels produced a higher optimal moisture content and increased resistance to shear force. This study showed that XG affects the mechanical properties of kaolinite through changing kaolinite fabrics (up to 0.5% of the XG-to-kaolinite mass ratio) and absorbing pore-fluids (excess XG over 0.5% of the XG-to-kaolinite mass ratio).

The global carbon dioxide (CO2) emissions and the increasing global warming have resulted in catastrophic climate change, including rising sea levels, heat waves, and rainfall imbalances1,2,3. To mitigate the concerns surrounding climate change, geotechnical engineers have conducted various studies to develop eco-friendly materials to replace the use of ordinary Portland cement (OPC) in soil improvement materials4. The OPC accounts for 5%–7% of anthropogenic CO2 emissions with one ton of CO2 emission for every ton of production5,6.

The biopolymer-based soil treatment (BPST), which uses exo-cultured biopolymers resulting from the metabolism of living organisms for soil improvement, has been extensively studied for integration as an environmentally friendly soil improvement technique7,8,9. The biopolymers affect soil grains by increasing the pore-fluid viscosity and particle interaction10. Based on the interaction of biopolymers and soils, biopolymers have shown their ability to enhance soil consistency11, coagulation12, soil strength13,14,15,16,17,18, surface erosion19,20,21,22, and hydraulic conductivity control23,24,25,26.

In the context of clays, the presence of biopolymers can lead to direct ionic bonding with the surface of clay particles27, resulting in modifications of the clay fabric, and geometric arrangement of the soil particles10,11. For instance, Mahamaya et al.28 investigated the effect of xanthan gum (XG), guar gum, and cellulose biopolymers on fly ash and mine tailings. The study demonstrated improvements in index properties, compressive strength, and water erosion resistance, attributed to morphological changes due to the interaction between the soil and the long-chained biopolymer strings. Similarly, Hamza et al.29 found that XG-induced clay aggregation enhanced geotechnical parameters of soils such as strength, consolidation, hydraulic conductivity, and freeze–thaw durability. Kang et al.30 compared the effects of various biopolymers on the settling characteristics of kaolinite and fly ashes, revealing that cationic biopolymers induced fabric changes in kaolinite through bridging and charge neutralization, resulting in an increased settling velocity. Microscopic techniques, including scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS), have been widely utilized in previous research to investigate the interactions between biopolymers and clays. However, electron microscopy techniques have practical limitations, including challenges in sample preparation and limited surface observation31, which hinder a comprehensive understanding of the biopolymer’s effect on the fabric of bulk clay materials.

To bridge this knowledge gap, this study aims to examine and analyze the fabric of XG biopolymer-treated kaolinite by employing X-ray diffraction (XRD) technique, as well as variations in its mechanical properties. XRD technique is extensively utilized for analyzing the structure of bulk clays due to its capability to probe depths of 30–50 μm32,33. Among a variety of organic polymers30, XG was selected in this study owing to its wide usage in various applications34,35,36, promising results in enhancing geotechnical properties13,37,38, and unique rheological properties such as the formation of viscous hydrogels and pseudoplastic behavior39,40. These characteristics make XG a suitable candidate for investigating its effects on the fabric and mechanical properties of kaolinite clay. Several experimental methods were used to achieve the study’s goal. The XRD patterns of XG-treated kaolinites were obtained to determine the fabric of clays by comparing the X-ray peaks and their amplitudes. By integrating SEM and environmental SEM (ESEM), this work visually examined the fabric of XG-treated kaolinite in dry and humid states. Based on visual observations, the compaction behavior and su of XG-treated kaolinites were analyzed to analyze the impact of XG on kaolinites’ fundamental properties.

Figure 1 depicts the XRD patterns of XG-treated kaolinites. The basic properties can be found in Extended Data Fig. 1 and Supplementary Table 1. The characteristic peaks are evident at diffraction angles in the order of 2θ = 12.31°, 24.84°, 20.34°, corresponding to the planes 001, 002, and 110 (Supplementary Table 2, and Extended Data Fig. 2). Here, the faces of the clay particles mostly consist of basal planes, and edges of clay particles mostly consist of prism planes41. The observed dominant basal peaks indicate that most clay particles are laminarly oriented, which is consistent with the report of Żbik et al.42. The surface charge of kaolinite primarily consists of silica facets, gibbsite facets, and edges. According to the reported isoelectric points of each surface43,44,45,46,47, the gibbsite facets and edges exhibit a positive charge, while the silica facets exhibit a negative charge within the pH range (5.3 ± 0.1) used in this study. Consequently, the negatively charged silica faces attract the positively charged gibbsite faces and edges, leading to the formation of face-to-face (FF) and edge-to-face (EF) fabric arrangements, respectively. The observed dominant basal peaks can be attributed to the higher surface area of the gibbsite faces compared to the edge surfaces.

X-ray diffraction patterns of XG-treated kaolinite showing (a) at all diffraction angles, (b,c) at basal peaks, (d,e) at prism peaks.

Variation in peak ratio with XG content at (a) basal and (b) prism peaks.

There is no major shift in the peak angle due to XG, indicating that the addition of XG in kaolinite has no substantial impact on the interlayer spaces between silicate layers as intercalation and exfoliation48. Instead, the XG content used in this study serves as a conventional composite filler, thus affecting the tactoids comprising several stacked silicate monolayers49. The XG-treatments change the intensity of basal and prism peaks. Kaolinites with 0.5% and 1.0% of XG-treatments showed a higher intensity of the basal peaks than the untreated kaolinite (Fig. 1b,c); however, all XG-treated kaolinites exhibited a reduction in the strength of the prism peaks compared to that of the untreated kaolinite (Fig. 1d,e). The change in peak strengths indicates that the XG affected the kaolinite properties because it transformed their fabrics50,51. Previous studies have highlighted the role of XG in promoting fabric transformation in kaolinite through its unique interaction with the clay surface, resulting in significant alterations in the hydro-mechanical properties of the clay11,52.

For a quantitative analysis of the variations in kaolinite fabrics with XG content, the relative intensities of each peak and the highest basal peaks—that is, the peak ratio (PR)—can be computed as follows53:

where I2θ denotes the intensity recorded at a diffraction angle of 2θ, and Imax denotes the specimen’s strongest intensity—that is, the 002 planes in this study. The results showed that the addition of XG had a negligible impact on the basal peaks (Fig. 2a) but reduced the peak ratio at prism peaks (Fig. 2b). Owing to the positioning of prism planes at the edges of clay particles54, higher prism peaks indicate that the geometric arrangement of kaolinite clay platelets was randomly oriented, implying the formation of EF contacts. In contrast, the observed reduction in the peak ratio at prism peaks indicates a more FF particle arrangement41, due to the influence of XG. Furthermore, XG of mb/ms = 0.5% exhibited the lowest PR at prism peaks, whereas the PR at prism peaks steadily increased with XG for mb/ms > 0.5%.

When considering the building of pavements, airports, levees, and dams, compaction characteristics are essential parameters that affect the mechanical properties of soils55. Figure 3 shows the results of standard Proctor compaction tests conducted on XG-treated kaolinites under varying mb/ms conditions. The compaction curve (Fig. 3a) shows that the XG decreases the variation in dry unit weight by w, which further indicates that XG reduces the soil’s sensitivity to variations in w56.

Compaction behavior of XG-treated kaolinite showing (a) the compaction curve, (b) the variation in optimal moisture content with XG, and (c) the variation in maximum dry density with XG.

The XG raises the optimal moisture content (OMC) (Fig. 3b) and lowers the maximum dry density (MDD) (Fig. 3c). This tendency can be attributed to the formation of an interconnecting network—that is, hydrogen bonding or direct electrical bonding—between the kaolinite particles10,57, resulting in a modification of the kaolinite fabrics as indicated by the XRD results, which resist the compaction energy16,56. Ni et al.58 also investigated the increase in OMC and the decrease in MDD with XG, indicating that this alteration is caused by the clay content and biopolymer characteristics. In the case wherein kaolinite is used, when the XG content (mb/ms) is > 0.5%, the observed OMC slightly decreases and the MDD increases. This trend is consistent with the work of Kang et al.59, which demonstrated a backbone trend at mb/ms = 0.1%. Specifically, mb/ms of 0.5% increases the OMC from 32.4% (untreated kaolinite) to 36%; however, the extra XG has a negligible impact on the OMC. Additionally, the MDD decreases as XG changes from 1.31 g/cm3 (untreated kaolinite) to 1.22 g/cm3 (mb/ms = 2.0%). These results match the previous findings that XG with mb/ms = 0.5% exhibit the local maximum liquid limits11,52 and su10.

Figure 4 shows the vane shear test results of XG-treated kaolinites in terms of su. At comparable water content, XG-treated kaolinites exhibit a higher su compared to untreated kaolinites. Based on the exponential relationship between w and su60, the results of the vane shear tests can be reduced to the parameters a and b, where parameter a denotes w at su = 1 kPa, while parameter b denotes the variation of w in response to a change in su. Parameters a and b increase with XG of mb/ms = 0.5%, suggesting that XG enhances the su at the same w while reducing its sensitivity to w fluctuations. Then, parameters decreased as XG content varied from 0.5 to 1.0%, and they increased again with XG treatment mb/ms > 1.0%.

Effect of XG on the undrained shear strength of compacted kaolinite.

The visual inspection of XG-treated clays shows the interaction between kaolinite and XG, which affects the fabrics and mechanical properties of kaolinites. Notably, the fabric distinctions resulting from XG treatment were analyzed using the higher resolution capabilities of SEM. In contrast, ESEM was employed to investigate the behavior of kaolinite treated with XG under different relative humidity conditions, despite the challenges associated with image quality, specifically contrast and brightness, which are influenced by chamber humidity61. By employing both SEM and ESEM methods and considering their combined results, previous research has achieved consistent findings62.

Compared to untreated kaolinite with random EE and EF associations (Fig. 5a), the XG in kaolinite produces interparticle bridges between kaolinite particles, inducing a higher degree of FF associations (Fig. 5b). Consequently, XG side chains interact with kaolinite via direct electrostatic attraction, ligand exchange, and hydrogen bonding27,63. Thus, the electrical interaction between XG and kaolinite particles leads to the creation of a bridge between particles11. When the XG powder is dissolved in water, the glucuronic and pyruvic acid groups on its side chains become active, and the molecule becomes negatively charged52,64,65. Under humid conditions, the XG side chain absorbs pore fluids and swells, resulting in its expansion. According to Dogan et al.66, XG absorbs approximately 25 g water per gram of XG. Consequently, XG forms bridges between the kaolinite particles, as shown in Fig. 5b. Additionally, XG absorbs the surrounding water molecules, as shown in Fig. 5c,d, leading to the generation of a viscous hydrogel around the kaolinite particles.

Microscopy observations of XG-treated kaolinites; SEM observations in a dry state for (a) untreated kaolinite and (b) XG 1%-treated kaolinite, and ESEM observations of XG 1%-treated kaolinite with a relative humidity of (c) 60%, and (d) 100%.

It was found that XG affected the kaolinite particle associations. Based on the XRD and microscopy observations, Fig. 6 schematically shows the potential impact of XG on the kaolinite fabrics. In the absence of XG (Fig. 6a), kaolinite tends to flocculate in FF and EF contacts because of the net-attraction energy between the negatively charged face surfaces and the positively charged gibbsite and edge surfaces63,67,68,69. This formation of EF contacts leads to greater prism peaks than those of XG-treated kaolinites (Fig. 1).

Kaolinite (a) without XG and (b) with XG.

In contrast, the XG-treated kaolinite form bridges between the kaolinite particles (Fig. 6b), which is evident in the microscopy images (Fig. 5b–d), resulting in more FF associations because of the electrostatic interaction with the kaolinite surface charges11,52. Consequently, the creation of XG-bridges peak at mb/ms = 0.5%, demonstrating the minimal PR at prism peaks (Fig. 2b). Meanwhile, when mb/ms is greater than 0.5%, the water absorption of the excess XG hydrogel hinders bridge formation40, leading to a higher PR at prism peaks. Notably, the PR at prism peaks for mb/ms = 1.0–2.0% is still lower than that of untreated kaolinite.

In summary, the formation of XG-bridges and viscous XG hydrogels alters the mechanical properties of kaolinite soils. The XG-bridges between kaolinite particles changes the kaolinite fabrics into FF associations, and this further improves their resistance to compaction energy and shear stress. At the same time, the water absorption by XG also contributes to the mechanical properties of kaolinite clays. The excess XG in the void space primarily absorbs pore fluids and swells, which is evident in the ESEM observations (Fig. 5)—that is, swollen XG absorbs water, increasing the hydrodynamic volume and subsequently leading to a rise in the viscosity of the pore fluids70. Increasing pore-fluid viscosity is associated with cohesion, shear strength, damping ratio, and shear modulus39,71,72. Thus, factors such as XG-bridges, cause of fabric modification, and XG hydrogel fill the spaces between clay particles, leading to a reduction in the MDD (Fig. 3c), and an increase in OMC (Fig. 3b) and su (Fig. 4). Additionally, XG water absorption makes the kaolinite less susceptible to variations in w. Accordingly, XG reduces the fluctuations in dry density (Fig. 3a) and su with increasing w (Parameter b in Fig. 4).

Notably, XG content of mb/ms = 0.5% exhibits a local minimum for XRD prism peaks (Fig. 2b) and a similar OMC with higher mb/ms (e.g., 2.0%) (Fig. 3b), as well as an optimal biopolymer content for LL11,52. Regarding the aforementioned factors, it can be hypothesized that XG content (mb/ms) below 0.5% interacts primarily with the kaolinite surfaces, changing their fabrics. Despite the hindered XG fabric rearrangement observed in Figs. 1 and 5 for XG content exceeding 0.5%, su continues to increase with higher mb/ms. This indicates the significant role of XG's water absorption characteristics in enhancing the shear resistance of kaolinite. Rather than directly interacting with the kaolinite particles, XG content exceeding 0.5% primarily interacts with water molecules. Consequently, the plasticity index decreases as mb/ms increases11. Notably, the plasticity index exhibits an inverse relationship with su60,73. Furthermore, this behavior depends on the biopolymer and clay characteristics23. For instance, Chang and Cho74 reported that gellan gum biopolymer showed the maximum shear strength with 4% of biopolymer-to-kaolinite content. Even for the XG treatment, their effect differed by clay types11.

This study analyzed the impact of XG on the fabrics of kaolinite clays based on XRD analyses, compaction tests, laboratory vane shear experiments, and microscopy observations. The experimental results showed that XG modified the kaolinite fabrics through electrical charge interactions with the kaolinite surfaces. The XRD analyses showed that XG resulted in a decrease in the number of peaks at prism planes, indicating that XG altered the association of kaolinites from EF to FF. Moreover, the XRD patterns exhibited local peaks at mb/ms = 0.5%. The SEM images also visually demonstrated XG-induced FF fabrics. In addition to XG-kaolinite interactions, the ESEM images indicated that the XG absorbed pore fluids and swelled. Evidently, the interactions between the XG, kaolinite, and water impacted the mechanical properties of the kaolinite clays. The XG-induced bridge formation between kaolinite particles enhanced the resistance of kaolinite to external forces. In void spaces, the XG absorbed pore fluids to produce viscous hydrogels. Owing to the complex interaction among XG, kaolinite, and pore fluids, the MDD decreased, and the OMC and su increased due to the XG treatment. A series of experimental analyses revealed that XG content (mb/ms) of 0.5% mainly affects the mechanical properties of kaolinite because it forms networks between kaolinite particles, while XG content (mb/ms) over 0.5% mainly absorbs pore fluids and increases the pore-fluid viscosity.

By investigating XG treatment effects on kaolinite, this study explores the potential applicability and performance of XG in geotechnical engineering applications. However, the unique mineral composition of kaolinite, characterized by its 1:1 layered tetrahedral and octahedral sheets, distinguishes it from other clay minerals with a 2:1 layered structure, such as illite and montmorillonite75. Owing to these distinct mineralogical characteristics, the specific properties associated with kaolinite may not directly apply to all engineering scenarios. Considering the diverse mineral composition of clays, future research should encompass the evaluation of other clay types to further enhance our understanding of their behavior and explore potential applications.

This study integrated kaolinite clay (Bintang, Indonesia) and XG biopolymer (CAS: 11138-66-2; Sigma Aldrich). Kaolinite—which comprises 1:1 layered tetrahedral and octahedral sheets—was chosen as a typical clay mineral because it is more responsive to fabric changes than 2:1 layered clay minerals76,77. Given kaolinite’s high width: thickness aspect ratio (3–18)78,79,80,81, the edge and face charge attraction is crucial for kaolinite fabrics and mechanical properties82. Moreover, kaolinite exhibits low cation adsorption because of the insignificant isomorphic substitution of Al3+ or Fe3+ for Si4+78,83. Although kaolinite possesses both pH-independent negative charges and pH-dependent charges, the overall charge characteristic becomes more positive at low pH values and more negative at high pH values84.

The XG is a biopolymer that is produced by the microbe Xanthomonas campestris, and its structure consists of repeated glucose units and side chains containing three sugar units85. The XG is a water-soluble biopolymer whose structure swells upon hydration via hydrogel bonding, the glucuronic (C6H10O7), and pyruvic acid (C3H4O3) groups on its side chain becoming negatively charged52,64,65. The XG is widely used as a thickening agent and a stabilizer for suspensions, solid particles, and foams86,87.

Supplementary Table 1 shows the index properties of kaolinite, indicating an increase in the LL and plastic limit (PL) with the addition of XG, as previously reported by Nugent, et al.52 and Chang et al.11. Bintang kaolinite is classified as clay with high plasticity (CH) according to the ASTM D2487 standard88. The kaolinite was dried in an oven at 110 °C to evaporate the pore fluids in clay matrixes prior to experiments, based on the ASTM D2216 standard89. In contrast, XG was used without pre-treatment. Extended Data Fig. 1 shows the particle size distribution curve of kaolinite and XG obtained using laser diffraction spectroscopy (Model HELOS/KR-H248, Sympatec GmbH, Clausthal-Zellerfeld, Germany) based on the ASTM D4464-15 and ASTM B822-20 standards90,91. The kaolinite particle shape was observed by scanning electron microscopy (Model SU5000, Hitachi, Tokyo, Japan).

The oven-dried kaolinite was mixed with XG powder at XG to the dry soil ratio in mass (mb/ms) of 0% (untreated), 0.5%, 1.0%, and 2.0%. Then, deionized water (DI) with pH of 6.2 ± 0.2 at 20 °C, with its designated water content (w), was added and thoroughly mixed until forming a uniform XG–clay–DI mixture. The pH of kaolinite was determined to be 5.3 ± 0.1 at 20 °C, following the guidelines outlined in the ASTM standard92.

The XG-treated kaolinites (mb/ms = 0%, 0.5%, 1.0%, and 2.0%) with a w of 35% (around the optimal moisture content (OMC)) were adhered to 18 mm × 18 mm cover glass (Marienfeld; Germany) and air-dried for 24 h at 20 °C. The XRD patterns of the XG-treated kaolinites were then collected using Cu K-alpha radiation of wavelength 0.154 nm, which were generated using a Rigaku SmartLab diffractometer (Rigaku, Japan) operated by a 9 kW X-ray generator.

Because the diffraction angle is a mineral-dependent feature, XRD techniques have been used to identify minerals93. The XRD measures the number of diffracted X-rays that impact a crystal of clay particles and outputs the clay textile identification based on Bragg's law—that is, nλ = 2d·sinθ; here, n denotes the order of reflection, λ denotes the wavelength, d denotes the particle spacing, and θ denotes the diffraction angle.

This study analyzed the XG-treated kaolinite fabrics in accordance with the methodologies proposed by Sachan and Penumadu41, wherein pure-kaolinite fabrics were recognized based on the basal and prism peaks of the XRD patterns as shown in Supplementary Table 2. Extended Data Fig. 2 depicts the basal and prism planes of a unit cell of kaolinite. The parallel orientation of platelets—that is, the FF associations—favors basal planes on the surface, resulting in a higher count at basal peaks. In contrast, the honeycomb orientation of platelets—that is, the EF associations—increases prism reflections and decreases basal planes.

The compaction characteristics of XG-treated kaolinite clay (mb/ms = 0%, 0.5%, 1.0%, and 2.0%) with a w of 15%–55% were analyzed using a standard Proctor compaction test. The XG-treated kaolinite mixtures were placed in a 0.95-l cylindrical mold and compacted by following the ASTM D698-12E2 standard. After compaction, the surface was flattened using a spatula. The final total soil weight was obtained. Next, the laboratory vane shear apparatus measured the su of compacted kaolinites.

After compaction, laboratory vane shear tests were conducted to analyze the XG-affected kaolinite fabrics (mb/ms = 0%, 0.5%, 1.0%, and 2.0%) on the su of kaolinite. The su of XG-treated kaolinites was determined by rotating a rectangular vane (width = 12.7 mm, height = 12.7 mm, and thickness = 0.05 mm) at the top, center, and bottom of the compacted specimen at a velocity of 60˚/min based on the ASTM D4648-05 standard95. Additionally, experiments were conducted in triplicate for each specimen to increase the reproducibility of the experimental data. Following the vane shear tests, the average w at each tested position was measured according to the ASTM D2216 standard89.

This study observed the microscale interactions between XG and kaolinite under dry and humid conditions, the relative humidity being 60% and 100%, respectively, using SEM (SU-5000, Hitachi High Technologies) and ESEM (Model Quattro ESEM, Thermo Fisher Scientific Inc., Waltham, USA). Untreated and treated kaolinites—that is, mb/ms = 0, 1.0%—at w = 35% were air-dried for 24 h at 20 °C and attached to a 25-mm diameter SEM mount using carbon conductive tabs (PELCO Tabs; Ted Pella, Inc.). Before SEM observations, the specimens were osmium (OsO4)-coated for 10 s under a vacuum using a plasma coater (OPC-60A).

The ESEM, which controls the water vapor pressure (10–4000 Pa) and the relative humidity in its specimen chamber96, was used to assess the variation of XG-treated kaolinite (mb/ms = 1%) using a change in the relative humidity. The samples (w = 35%) were initially attached to an ESEM mount, and the specimen surfaces were exposed to the electron beams thereafter. During the observations, the relative humidity fluctuated between 0 and 100%.

The data that support the findings of this study are available from the authors upon reasonable request.

Biopolymer-based soil treatment

Liquid limit (%)

Plastic limit (%)

Undrained shear strength (kPa)

Edge-to-face association

Face-to-face association

Scanning electron microscopy

Transmission electron microscopy

Xanthan gum

Environmental scanning electron microscopy

Mean particle diameter (μm)

Specific surface area (m2/g)

Cations exchange capacity (meq/100 g)

XG-to-dry soil ratio in mass (%)

Water content (%)

Optimal moisture content (%)

Maximum dry density (g/cm3)

Deionized water

X-ray diffraction analysis

Relative intensities of each XRD peak and the highest basal peaks (–)

Water content at the undrained shear strength of 1 kPa (%)

Variation of water content at a change in the undrained shear strength (–)

Pan, L. et al. Rapid postglacial rebound amplifies global sea level rise following West Antarctic Ice Sheet collapse. Sci. Adv. 7, eabf7787. https://doi.org/10.1126/sciadv.abf7787 (2021).

Article ADS PubMed PubMed Central Google Scholar

Hansen, J. et al. Assessing “dangerous climate change”: Required reduction of carbon emissions to protect young people, future generations and nature. PLoS One 8, e81648. https://doi.org/10.1371/journal.pone.0081648 (2013).

Article ADS CAS PubMed PubMed Central Google Scholar

Matthews, H. D., Gillett, N. P., Stott, P. A. & Zickfeld, K. The proportionality of global warming to cumulative carbon emissions. Nature 459, 829–832. https://doi.org/10.1038/nature08047 (2009).

Article ADS CAS PubMed Google Scholar

DeJong, J. T., Mortensen, B. M., Martinez, B. C. & Nelson, D. C. Bio-mediated soil improvement. Ecol. Eng. 36, 197–210. https://doi.org/10.1016/j.ecoleng.2008.12.029 (2010).

Article Google Scholar

Caldeira, K. & Kasting, J. F. Insensitivity of global warming potentials to carbon dioxide emission scenarios. Nature 366, 251–253. https://doi.org/10.1038/366251a0 (1993).

Article ADS CAS Google Scholar

Matthews, H. D. & Caldeira, K. Stabilizing climate requires near-zero emissions. Geophy. Res. Lett. https://doi.org/10.1029/2007GL032388 (2008).

Article Google Scholar

Chang, I. et al. Review on biopolymer-based soil treatment (BPST) technology in geotechnical engineering practices. Transp. Geotech. 24, 100385. https://doi.org/10.1016/j.trgeo.2020.100385 (2020).

Article Google Scholar

Ashraf, M. S., Azahar, S. B. & Yusof, N. Z. in IOP Conference Series: Materials Science and Engineering. 012058 (IOP Publishing).

Seo, S. et al. Site application of biopolymer-based soil treatment (BPST) for slope surface protection: In-situ wet-spraying method and strengthening effect verification. Constr. Build. Mater. 307, 124983. https://doi.org/10.1016/j.conbuildmat.2021.124983 (2021).

Article CAS Google Scholar

Chang, I., Kwon, Y.-M. & Cho, G.-C. Effect of pore-fluid chemistry on the undrained shear strength of xanthan gum biopolymer-treated clays. J. Geotech. Geoenviron. 147, 06021013. https://doi.org/10.1061/(ASCE)GT.1943-5606.0002652 (2021).

Article CAS Google Scholar

Chang, I., Kwon, Y.-M., Im, J. & Cho, G.-C. Soil consistency and interparticle characteristics of xanthan gum biopolymer–containing soils with pore-fluid variation. Can. Geotech. J. 56, 1206–1213. https://doi.org/10.1139/cgj-2018-0254 (2019).

Article CAS Google Scholar

Kwon, Y.-M., Im, J., Chang, I. & Cho, G.-C. ε-polylysine biopolymer for coagulation of clay suspensions. Geomech. Eng. 12, 753–770. https://doi.org/10.12989/gae.2017.12.5.753 (2017).

Article Google Scholar

Chang, I., Im, J., Prasidhi, A. K. & Cho, G.-C. Effects of xanthan gum biopolymer on soil strengthening. Constr. Build. Mater. 74, 65–72. https://doi.org/10.1016/j.conbuildmat.2014.10.026 (2015).

Article Google Scholar

Chang, I., Prasidhi, A. K., Im, J. & Cho, G.-C. Soil strengthening using thermo-gelation biopolymers. Constr. Build. Mater. 77, 430–438. https://doi.org/10.1016/j.conbuildmat.2014.12.116 (2015).

Article Google Scholar

Chang, I. & Cho, G.-C. Strengthening of Korean residual soil with β-1,3/1,6-glucan biopolymer. Constr. Build. Mater. 30, 30–35. https://doi.org/10.1016/j.conbuildmat.2011.11.030 (2012).

Article Google Scholar

Kwon, Y.-M., Chang, I., Lee, M. & Cho, G.-C. Geotechnical engineering behaviors of biopolymer-treated soft marine soil. Geomech. Eng. 17, 453–464. https://doi.org/10.12989/GAE.2019.17.5.453 (2019).

Article Google Scholar

Cabalar, A. F., Awraheem, M. H. & Khalaf, M. M. Geotechnical properties of a low-plasticity clay with biopolymer. J. Mater. Civil Eng. 30, 04018170. https://doi.org/10.1061/(ASCE)MT.1943-5533.0002380 (2018).

Article Google Scholar

Lee, M., Kwon, Y.-M., Park, D.-Y., Chang, I. & Cho, G.-C. Durability and strength degradation of xanthan gum based biopolymer treated soil subjected to severe weathering cycles. Sci. Rep. 12, 19453. https://doi.org/10.1038/s41598-022-23823-4 (2022).

Article ADS CAS PubMed PubMed Central Google Scholar

Kwon, Y.-M., Ham, S.-M., Kwon, T.-H., Cho, G.-C. & Chang, I. Surface-erosion behaviour of biopolymer-treated soils assessed by EFA. Géotech. Lett. 10, 1–7. https://doi.org/10.1680/jgele.19.00106 (2020).

Article Google Scholar

Kavazanjian, E., Iglesias, E. & Karatas, I. in The 17th International Conference on Soil Mechanics and Geotechnical Engineering (eds Hamza, M., Shahien, M., & El-Mossallamy, Y.) 881–884 (IOS Press, 2009).

Orts, W. J., Sojka, R. E., Glenn, G. M. & Gross, R. A. in Biopolymers from Polysaccharides and Agroproteins, ACS Symposium Series Ch. 6, Vol. 786, 102–116 (American Chemical Society, 2001).

Kwon, Y.-M., Cho, G.-C., Chung, M.-K. & Chang, I. Surface erosion behavior of biopolymer-treated river sand. Geomech. Eng. 25, 49–58. https://doi.org/10.12989/gae.2021.25.1.049 (2021).

Article Google Scholar

Ayeldeen, M. K., Negm, A. M. & El Sawwaf, M. A. Evaluating the physical characteristics of biopolymer/soil mixtures. Arab. J. Geosci. 9, 1–13. https://doi.org/10.1007/s12517-016-2366-1 (2016).

Article CAS Google Scholar

Cabalar, A. F., Wiszniewski, M. & Skutnik, Z. Effects of xanthan gum biopolymer on the permeability, odometer, unconfined compressive and triaxial shear behavior of a sand. Soil Mech. Found. Eng. 54, 356–361. https://doi.org/10.1007/s11204-017-9481-1 (2017).

Article Google Scholar

Chang, I., Im, J. & Cho, G.-C. Geotechnical engineering behaviors of gellan gum biopolymer treated sand. Can. Geotech. J. 53, 1658–1670. https://doi.org/10.1139/cgj-2015-0475 (2016).

Article CAS Google Scholar

Kwon, Y.-M., Chang, I. & Cho, G.-C. Consolidation and swelling behavior of kaolinite clay containing xanthan gum biopolymer. Acta Geotech. https://doi.org/10.1007/s11440-023-01794-8 (2023).

Article Google Scholar

Theng, B. K. G. Formation and Properties of Clay–Polymer Complexes Vol. 4 (Elsevier, 2012).

Google Scholar

Mahamaya, M., Das, S. K., Reddy, K. R. & Jain, S. Interaction of biopolymer with dispersive geomaterial and its characterization: An eco-friendly approach for erosion control. Journal of Cleaner Production 312, 127778. https://doi.org/10.1016/j.jclepro.2021.127778 (2021).

Article CAS Google Scholar

Hamza, M. et al. Geotechnical behavior of high-plastic clays treated with biopolymer: Macro–micro-study. Environ Earth Sci 82, 91. https://doi.org/10.1007/s12665-023-10760-2 (2023).

Article ADS Google Scholar

Kang, X., Xia, Z., Chen, R., Sun, H. & Yang, W. Effects of inorganic ions, organic polymers, and fly ashes on the sedimentation characteristics of kaolinite suspensions. Appl. Clay Sci. 181, 105220. https://doi.org/10.1016/j.clay.2019.105220 (2019).

Article CAS Google Scholar

Barden, L. & Sides, G. Sample disturbance in the investigation of clay structure. Géotechnique 21, 211–222. https://doi.org/10.1680/geot.1971.21.3.211 (1971).

Article CAS Google Scholar

Archer, D. X-Ray Diffraction of Deep-Sea Clay Minerals, Ph. D. Thesis, University of Manchester (1969).

Brindley, G. W. An X-ray method for studying orientation of micaceous minerals in shales, clays, and similar materials. Mineral. Mag. J. Mineral. Soc. 30, 71–78. https://doi.org/10.1180/minmag.1953.030.220.08 (1953).

Article ADS CAS Google Scholar

Williams, B. P., Pinge, S., Kim, Y.-K., Kim, J. & Joo, Y. L. Enhanced dispersion and stability of petroleum coke water slurries via triblock copolymer and xanthan gum: Rheological and adsorption studies. Langmuir 31, 8989–8997. https://doi.org/10.1021/acs.langmuir.5b01573 (2015).

Article CAS PubMed Google Scholar

Sworn, G. Chapter 27—Xanthan Gum in Handbook of Hydrocolloids (Woodhead Publishing, 2021).

Google Scholar

Tempio, J. S. & Zatz, J. L. Flocculation effect of xanthan gum in pharmaceutical suspensions. J. Pharm. Sci. 69, 1209–1214. https://doi.org/10.1002/jps.2600691024 (1980).

Article CAS PubMed Google Scholar

Kwon, Y.-M., Moon, J.-H., Cho, G.-C., Kim, Y.-U. & Chang, I. Xanthan gum biopolymer-based soil treatment as a construction material to mitigate internal erosion of earthen embankment: A field-scale. Constr. Build. Mater. 389, 131716. https://doi.org/10.1016/j.conbuildmat.2023.131716 (2023).

Article CAS Google Scholar

Kwon, Y.-M., Kang, S.-J., Cho, G.-C. & Chang, I. Effect of microbial biopolymers on the sedimentation behavior of kaolinite. Geomech. Eng. 33, 121–131. https://doi.org/10.12989/gae.2023.33.2.121 (2023).

Article Google Scholar

Wyatt, N. B. & Liberatore, M. W. Rheology and viscosity scaling of the polyelectrolyte xanthan gum. J. Appl. Polym. Sci. 114, 4076–4084. https://doi.org/10.1002/app.31093 (2009).

Article CAS Google Scholar

Whitcomb, P. J. & Macosko, C. W. Rheology of xanthan gum. J. Rheol. 22, 493–505. https://doi.org/10.1122/1.549485 (1978).

Article ADS CAS Google Scholar

Sachan, A. & Penumadu, D. Identification of microfabric of kaolinite clay mineral using X-ray diffraction technique. Geotech. Geol. Eng. 25, 603–616. https://doi.org/10.1007/s10706-007-9133-8 (2007).

Article Google Scholar

Żbik, M. S., Raftery, N. A., Smart, R. S. C. & Frost, R. L. Kaolinite platelet orientation for XRD and AFM applications. Appl. Clay Sci. 50, 299–304. https://doi.org/10.1016/j.clay.2010.08.010 (2010).

Article CAS Google Scholar

Kumar, N., Andersson, M. P., van den Ende, D., Mugele, F. & Siretanu, I. Probing the surface charge on the basal planes of kaolinite particles with high-resolution atomic force microscopy. Langmuir 33, 14226–14237. https://doi.org/10.1021/acs.langmuir.7b03153 (2017).

Article CAS PubMed PubMed Central Google Scholar

Pecini, E. M. & Avena, M. J. Measuring the isoelectric point of the edges of clay mineral particles: The case of montmorillonite. Langmuir 29, 14926–14934. https://doi.org/10.1021/la403384g (2013).

Article CAS PubMed Google Scholar

Williams, D. J. A. & Williams, K. P. Electrophoresis and zeta potential of kaolinite. J. Colloid Interface Sci. 65, 79–87. https://doi.org/10.1016/0021-9797(78)90260-6 (1978).

Article ADS CAS Google Scholar

Santamarina, J. C., Klein, K. A., Palomino, A. & Guimaraes, M. S. in Chemical Behaviour: Chemo-Mechanical Coupling from Nano-structure to Engineering Applications 47–64 (2002).

Tajana, P., Ahmed, A., Gilles, M. & Johannes, L. in Clays, Clay Minerals and Ceramic Materials Based on Clay Minerals (ed Morari do, N. G.) Ch. 3 (IntechOpen, 2016).

Penaloza, D. Review on the preparation, structure and property relation of clay-based polymer nanocomposites. Kimika (J. Chem. Soc. Philipp.) 28, 44–56. https://doi.org/10.26534/kimika.v28i1.44-56 (2017).

Article Google Scholar

Sinha Ray, S. & Bousmina, M. Biodegradable polymers and their layered silicate nanocomposites: In greening the 21st century materials world. Progress in Materials Science 50, 962–1079. https://doi.org/10.1016/j.pmatsci.2005.05.002 (2005).

Article CAS Google Scholar

Gruner, J. W. The crystal structure of kaolinite. Zeitschrift für Kristallographie Cryst. Mater. 83, 75–88. https://doi.org/10.1524/zkri.1932.83.1.75 (1932).

Article CAS Google Scholar

Gillott, J. E. Fabric of Leda clay investigated by optical, electron-optical, and X-ray diffraction methods. Eng. Geol. 4, 133–153. https://doi.org/10.1016/0013-7952(70)90009-8 (1970).

Article Google Scholar

Nugent, R. A., Zhang, G. & Gambrell, R. P. Effect of exopolymers on the liquid limit of clays and its engineering implications. Transp. Res. Record 2101, 34–43. https://doi.org/10.3141/2101-05 (2009).

Article Google Scholar

Sachan, A. & Penumadu, D. Effect of shear deformation on microfabric of clay using XRD technique. Geotech. Geol. Eng. 27, 249–264. https://doi.org/10.1007/s10706-008-9226-z (2009).

Article Google Scholar

Jaradat, K. A. et al. Heating-freezing effects on the orientation of kaolin clay particles. Appl. Clay Sci. 150, 163–174. https://doi.org/10.1016/j.clay.2017.09.028 (2017).

Article CAS Google Scholar

Ayeldeen, M., Negm, A., El-Sawwaf, M. & Kitazume, M. Enhancing mechanical behaviors of collapsible soil using two biopolymers. Journal of Rock Mechanics and Geotechnical Engineering 9, 329–339. https://doi.org/10.1016/j.jrmge.2016.11.007 (2017).

Article Google Scholar

Sujatha, E. R., Atchaya, S., Sivasaran, A. & Keerdthe, R. S. Enhancing the geotechnical properties of soil using xanthan gum—An eco-friendly alternative to traditional stabilizers. Bull. Eng. Geol. Environ. https://doi.org/10.1007/s10064-020-02010-7 (2020).

Article Google Scholar

Dontsova, K. M. & Bigham, J. M. Anionic polysaccharide sorption by clay minerals. Soil Sci. Soc. Am. J. 69, 1026–1035. https://doi.org/10.2136/sssaj2004.0203 (2005).

Article ADS CAS Google Scholar

Ni, J., Li, S. S., Ma, L. & Geng, X. Y. Performance of soils enhanced with eco-friendly biopolymers in unconfined compression strength tests and fatigue loading tests. Constr. Build. Mater. 263, 120039. https://doi.org/10.1016/j.conbuildmat.2020.120039 (2020).

Article CAS Google Scholar

Kang, X., Bate, B., Chen, R.-P., Yang, W. & Wang, F. Physicochemical and mechanical properties of polymer-amended kaolinite and fly ash–kaolinite mixtures. J. Mater. Civ. Eng. 31, 04019064. https://doi.org/10.1061/(ASCE)MT.1943-5533.0002705 (2019).

Article CAS Google Scholar

Koumoto, T. & Houlsby, G. T. Theory and practice of the fall cone test. Géotechnique 51, 701–712. https://doi.org/10.1680/geot.2001.51.8.701 (2001).

Article Google Scholar

Maison, T., Laouafa, F. & Fleureau, J.-M. in UNSAT 2010, International Conference on unsaturated soils. 525–530 (CRC Press).

Lin, B. & Cerato, A. B. Applications of SEM and ESEM in microstructural investigation of shale-weathered expansive soils along swelling-shrinkage cycles. Eng. Geol. 177, 66–74. https://doi.org/10.1016/j.enggeo.2014.05.006 (2014).

Article Google Scholar

Brady, P. V., Cygan, R. T. & Nagy, K. L. Molecular controls on kaolinite surface charge. J. Colloid Interface Sci. 183, 356–364. https://doi.org/10.1006/jcis.1996.0557 (1996).

Article ADS CAS PubMed Google Scholar

Hassler, R. A. & Doherty, D. H. Genetic engineering of polysaccharide structure: Production of variants of xanthan gum in Xanthomonas campestris. Biotechnol. Prog. 6, 182–187. https://doi.org/10.1021/bp00003a003 (1990).

Article CAS PubMed Google Scholar

Petri, D. F. S. Xanthan gum: A versatile biopolymer for biomedical and technological applications. J. Appl. Polym. Sci. https://doi.org/10.1002/app.42035 (2015).

Article Google Scholar

Dogan, M., Toker, O. S. & Goksel, M. Rheological behaviour of instant hot chocolate beverage: Part 1. Optimization of the effect of different starches and gums. Food Biophys. 6, 512–518. https://doi.org/10.1007/s11483-011-9233-0 (2011).

Article Google Scholar

Wang, Y. H. & Siu, W. K. Structure characteristics and mechanical properties of kaolinite soils. I. Surface charges and structural characterizations. Can. Geotech. J. 43, 587–600. https://doi.org/10.1139/t06-026 (2006).

Article CAS Google Scholar

Zbik, M. S., Smart, R. S. C. & Morris, G. E. Kaolinite flocculation structure. J. Colloid Interface Sci. 328, 73–80. https://doi.org/10.1016/j.jcis.2008.08.063 (2008).

Article ADS CAS PubMed Google Scholar

Fam, M. & Santamarina, J. C. A study of consolidation using mechanical and electromagnetic waves. Geotechnique 47, 203–219 (1997).

Article Google Scholar

Tan, X., Hu, L., Reed, A., Furukawa, Y. & Zhang, G. Flocculation and particle size analysis of expansive clay sediments affected by biological, chemical, and hydrodynamic factors. Ocean Dyn. 64, 143–157. https://doi.org/10.1007/s10236-013-0664-7 (2014).

Article ADS Google Scholar

Wang, Y.-H. & Siu, W.-K. Structure characteristics and mechanical properties of kaolinite soils. II. Effects of structure on mechanical properties. Can. Geotech. J. 43, 601–617. https://doi.org/10.1139/t06-027 (2006).

Article CAS Google Scholar

Eren, N. M., Santos, P. H. S. & Campanella, O. Mechanically modified xanthan gum: Rheology and polydispersity aspects. Carbohydr. Polym. 134, 475–484. https://doi.org/10.1016/j.carbpol.2015.07.092 (2015).

Article CAS PubMed Google Scholar

Houston, W. N. & Mitchell, J. K. Property interrelationships in sensitive clays. J. Soil Mech. Found. Div. 95, 1037–1062. https://doi.org/10.1061/JSFEAQ.0001303 (1969).

Article Google Scholar

Chang, I. & Cho, G.-C. Shear strength behavior and parameters of microbial gellan gum-treated soils: From sand to clay. Acta Geotech. 14, 361–375. https://doi.org/10.1007/s11440-018-0641-x (2019).

Article Google Scholar

Mitchell, J. K. & Soga, K. Fundamentals of Soil Behavior 3rd edn. (Wiley, 2005).

Google Scholar

Sridharan, A. & Rao, G. V. Shear strength behaviour of saturated clays and the role of the effective stress concept. Geotechnique 29, 177–193. https://doi.org/10.1680/geot.1979.29.2.177 (1979).

Article Google Scholar

Jang, J. & Santamarina, J. C. Fines classification based on sensitivity to pore-fluid chemistry. J. Geotech. Geoenviron. https://doi.org/10.1061/(ASCE)GT.1943-5606.0001420 (2016).

Article Google Scholar

Tombácz, E. & Szekeres, M. Surface charge heterogeneity of kaolinite in aqueous suspension in comparison with montmorillonite. Appl. Clay Sci. 34, 105–124. https://doi.org/10.1016/j.clay.2006.05.009 (2006).

Article CAS Google Scholar

Villanueva, M. P., Cabedo, L., Lagarón, J. M. & Giménez, E. Comparative study of nanocomposites of polyolefin compatibilizers containing kaolinite and montmorillonite organoclays. J. Appl. Polym. Sci. 115, 1325–1335. https://doi.org/10.1002/app.30278 (2010).

Article CAS Google Scholar

Beckett, R., Murphy, D., Tadjiki, S., Chittleborough, D. J. & Calvin Giddings, J. Determination of thickness, aspect ratio and size distributions for platey particles using sedimentation field-flow fractionation and electron microscopy. Colloids Surf. Physicochem. Eng. Asp. 120, 17–26. https://doi.org/10.1016/S0927-7757(96)03716-8 (1997).

Article CAS Google Scholar

Nadeau, P. H. The physical dimensions of fundamental clay particles. Clay Miner. 20, 499–514. https://doi.org/10.1180/claymin.1985.020.4.06 (1985).

Article ADS Google Scholar

Penner, D. & Lagaly, G. Influence of anions on the rheological properties of clay mineral dispersions. Appl. Clay Sci. 19, 131–142. https://doi.org/10.1016/S0169-1317(01)00052-7 (2001).

Article CAS Google Scholar

Zhou, Z. & Gunter, W. D. The nature of the surface charge of kaolinite. Clays Clay Miner. 40, 365–368. https://doi.org/10.1346/CCMN.1992.0400320 (1992).

Article ADS CAS Google Scholar

Au, P.-I. & Leong, Y.-K. Surface chemistry and rheology of slurries of kaolinite and montmorillonite from different sources. KONA Powder Part. J. https://doi.org/10.14356/kona.2016007 (2016).

Article Google Scholar

Garcia-Ochoa, F., Santos, V. E., Casas, J. A. & Gómez, E. Xanthan gum: production, recovery, and properties. Biotechnol. Adv. 18, 549–579. https://doi.org/10.1016/S0734-9750(00)00050-1 (2000).

Article CAS PubMed Google Scholar

Chang, I., Im, J. & Cho, G. C. Introduction of microbial biopolymers in soil treatment for future environmentally-friendly and sustainable geotechnical engineering. Sustainability 8, 251. https://doi.org/10.3390/su8030251 (2016).

Article Google Scholar

Katzbauer, B. Properties and applications of xanthan gum. Polym. Degrad. Stab. 59, 81–84. https://doi.org/10.1016/S0141-3910(97)00180-8 (1998).

Article CAS Google Scholar

ASTM. in ASTM Volume 04.08 Soil and Rock (I)L D420-D5876 Vol. 04.08 (ASTM International, 2017).

ASTM. in ASTM Volume 04.08 Soil and Rock (I): D420-D5876 (ASTM International, 2019).

ASTM. in ASTM Volume 04.08 Soil and Rock (I): D420-D5876 (ASTM International, 2020).

ASTM. in ASTM Volume 02.05: Metallic And Inorganic Coatings; Metal Powders And Metal Powder Products (ASTM International, 2020).

ASTM. in ASTM Volume 04.08 Soil and Rock (I): D420-D5876 (ASTM International, 2019).

Harris, W. & Norman White, G. in Methods of Soil Analysis Part 5—Mineralogical Methods 81–115 (2008).

ASTM. in ASTM Volume 04.08 Soil and Rock (I): D420-D5876 (ASTM International, 2012).

ASTM. in ASTM Volume 04.08 Soil and Rock (I): D420-D5876 (ASTM International, 2016).

Carrier, B. et al. ESEM study of the humidity-induced swelling of clay film. Langmuir 29, 12823–12833. https://doi.org/10.1021/la402781p (2013).

Article CAS PubMed Google Scholar

Download references

This work was supported by the National Research Foundation of Korea (NRF) Grants funded by the Korea Government (MSIT) (No. 2023R1A2C300559611 and No. 2022R1A2C2091517). We would like to thank Editage [http://www.editage.com] for editing and reviewing this manuscript for English language.

Department of Civil and Environmental Engineering, Northwestern University, Evanston, IL, 60208, USA

Yeong-Man Kwon

Department of Civil Systems Engineering, Ajou University, Suwon, 16499, Republic of Korea

Ilhan Chang

Department of Civil and Environmental Engineering, Korea Advanced Institute of Science and Technology (KAIST), Daejeon, 34141, Republic of Korea

Gye-Chun Cho

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

Y.M.K., I.C., and G.C.C. designed the concepts and experiments. Y.M.K. conducted the XRD analysis, standard Proctor test, microscopic observation, and vane shear tests. Y.M.K. prepared the manuscript under the supervision of G.C.C., and I.C.

Correspondence to Ilhan Chang or Gye-Chun Cho.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Kwon, YM., Chang, I. & Cho, GC. Xanthan biopolymer-based soil treatment effect on kaolinite clay fabric and structure using XRD analysis. Sci Rep 13, 11666 (2023). https://doi.org/10.1038/s41598-023-38844-w

Download citation

Received: 24 September 2022

Accepted: 16 July 2023

Published: 19 July 2023

DOI: https://doi.org/10.1038/s41598-023-38844-w

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.